| Customization: | Available |
|---|---|
| Type: | Stainless Steel Coils |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Specifications
| Standard | ASTM A240, JIS G4304, G4305, GB/T 4237, GB/T 8165, BS 1449, DIN17460, DIN 17441 |
|
Grade
|
200series&300series&400series |
| Thickness | 0.4mm-50mm |
| Width | 1000/1219/1500/1800mm |
| Surface finish | 2B, BA, 8K, 6K, Mirror Finished, No1, No2, No4, Hair Line with PVC |
| Manufacture technology | Manufacture technology |
| Loading Port | Tianjin Xingang |
| Delivery term | FOB Tianjin Xingang, CIF |
| Delivery lead time | 7~15days after received T/T or L/C. |
| Payment term | T/T 30% down payment, then L/C or T/T based on copy of B/L |
| Quality assurance | Mill Test Certificate is supplied with shipment, third Party Inspection is acceptable. |
| Packing | bundled with steel strips,then in wooden pallet,about 10kgs every wooden pallet add wrapped. or as customers requirement. |
| Strength of extension (Mpa) | 620 MIN |
| Yield strength (Mpa) | 310 MIN |
| Elongation (%) | 30 MIN |
| Area reduction(%) | 40 MIN |
| Density | 7.93 g/cm3 |
| Surface | Characteristics | Application |
| BA | Bright heat treatment after cold rolling. | Kitchen utensil, Kitchen ware, Architectural purpose. |
| 2B | Finished by heat treatment, pickling after cold rolling, followed by skin pass line to more brighter and smooth surface. |
General application medical instruments, Tableware. |
| NO.1 | Finished by hot-rolling, annealing and pickling, characterized by white pickled surface. |
Chemical industry equipment, Industrial tanks. |
| 8K(mirror) | A mirrorlike reflective surface by polishing with finer abrasives over 800 mesh. |
Refletor, Mirror, Interior- Exterior decoration for building. |
| Hair Line | Finished by continuous linear polishing. | Architecture industries, Escalators, Kitchen ware, Vehicles. |
Chemical compositions
| Grade | C ≤ | Si ≤ | Mn ≤ | P ≤ | S ≤ | Ni ≤ | Cr ≤ |
| 201 | 0.12 | 0.75 | 7.00 | 0.045 | 0.045 | 1.00-1.28 | 13.70-15.70 |
| 202 | 0.15 | 1.00 | 2.25 | 0.045 | 0.045 | 4.07-4.17 | 14.00-16.00 |
| 304 | 0.08 | 0.75 | 2.00 | 0.045 | 0.03 | 8.00-11.00 | 18.00-20.00 |
| 304L | 0.035 | 0.75 | 2.00 | 0.045 | 0.03 | 8.00-13.00 | 18.00-20.00 |
| 309 | 0.15 | 0.75 | 2.00 | 0.045 | 0.03 | 12.00-15.00 | 22.00-24.00 |
| 310S | 0.08 | 1.50 | 2.00 | 0.045 | 0.03 | 19.00-22.00 | 24.00-26.00 |
| 316 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 |
| 316L | 0.035 | 0.75 | 2.00 | 0.045 | 0.03 | 10.00-15.00 | 16.00-18.00 |
| 321 | 0.04-0.10 | 0.75 | 2.00 | 0.045 | 0.03 | 9.00-13.00 | 17.00-20.00 |
| 405 | 0.08 | 0.75 | 1.00 | 0.045 | 0.03 | 0.06 | 11.5-13.5 |
| 409 | 0.089 | 1.00 | 1.00 | 0.045 | 0.05 | 0.06 | 10.50-11.75 |
| 410 | 0.15 | 0.75 | 1.00 | 0.045 | 0.03 | 0.06 | 11.5-13.5 |
| 420 | 0.16-0.25 | 1.00 | 1.00 | 0.040 | 0.03 | 0.06 | 12.00-14.00 |
| 430 | 0.12 | 0.75 | 1.00 | 0.045 | 0.03 | 0.06 | 16.00-18.00 |
| 904L | 0.02 | 1.0 | 2.00 | 0.045 | 0.03 | 23.00-28.00 | 19.00-23.00 |
Packaging Details:
1, First layer, film wrapped
2, Second layer, Paper interleaved
3, Third layer, Corrugated Paper
4,Outside Plastic Package. Inside with steel protection circles.
5. Or accoding to customer's request
Looking forward to your inquiry anytime (7*24hours online service-Always for you)
){kind=link}